Τίτλος:	Polarization mechanisms and structural rearrangements in thermally poled sodium-alumino phosphate glasses
Δημιουργός/Συγγραφέας:	Dussauze, Marc Rodriguez, Vincent Velli, Leoni [EL] Βαρσάμης, Χρήστος-Πλάτων Ε.[EN] Varsamis, Christos-Platon E. [EL] Καμίτσος, Ευστράτιος Ι.[EN] Kamitsos, Efstratios I.
Εκδότης:	American Institute of Physics
Τόπος έκδοσης:	MELVILLE
Ημερομηνία:	2010-02-15
Γλώσσα:	Αγγλικά
ISSN:	0021-8979
DOI:	10.1063/1.3305318
Περίληψη:	Thermally poled glasses of composition 0.20Na(2)O-0.15Al(2)O(3)-0.65P(2)O(5) were investigated by second harmonic generation (SHG) to characterize the induced second order optical nonlinearities (chi(2)), and by infrared reflectance and micro-Raman spectroscopy to probe structural rearrangements in the nonlinear optical (NLO) layer. The SHG signals showed anodic and bulk chi(2) contributions, with the anodic response being one order of magnitude stronger. Also, a good agreement was found between the thickness of the NLO anodic layer (approximately 3 mu m) and the depth where structural changes were detected. The latter include the destruction of bonds between phosphorus and nonbridging oxygen atoms, this process leads to the release and migration of sodium cations and oxide anions and to the enhancement of glass network connectivity in the anodic NLO layer.
Τίτλος πηγής δημοσίευσης:	Journal of Applied Physics
Τόμος/Κεφάλαιο:	107
Τεύχος:	4
Σελίδες:	[6]
Θεματική Κατηγορία:	[EL] Φυσική[EN] Physics
Λέξεις-Κλειδιά:	aluminium compounds glass structure light polarisation optical harmonic generation phosphate glasses photoreflectance Raman spectra sodium compounds Physics, Applied
Αξιολόγηση από ομότιμους (peer reviewed):	Ναι
Κάτοχος πνευματικών δικαιωμάτων:	© AMER INST PHYSICS
Ηλεκτρονική διεύθυνση περιοδικού (link) :	http://jap.aip.org/jap/staff.jsp
Εμφανίζεται στις συλλογές:	Ινστιτούτο Θεωρητικής και Φυσικής Χημείας (ΙΘΦΧ) - Επιστημονικό έργο