Τίτλος: Synthesis, thermal and structural properties of pure TeO2 glass and zinc-tellurite glasses
Δημιουργός/Συγγραφέας: Tagiara N.S.
[EL] Παλλές, Δημήτρης[EN] Palles, Dimitrissemantics logo
[EL] Σημαντήρας, Eμμανουήλ[EN] Simandiras, Emmanuel D.semantics logo
Psycharis V.
Kyritsis A.
[EL] Καμίτσος, Ευστράτιος Ι.[EN] Kamitsos, Efstratios I.semantics logo
Εκδότης: Elsevier B.V.
Ημερομηνία: 2017
Γλώσσα: Αγγλικά
ISSN: 0022-3093
DOI: 10.1016/j.jnoncrysol.2016.11.033
Περίληψη: We have synthesized pure TeO2 glass and glasses in the systems xZnO − (1 − x)TeO2 (0 ≤ x ≤ 0.50) and yAl2O3 − (1 − y)TeO2 (0 ≤ y ≤ 0.03) by melting in Pt crucibles, and measured their glass transition temperature (Tg), density (ρ) and Raman spectra to correlate glass properties with structure. For pure TeO2 glass, synthesized using our newly developed intermittent quenching technique, we find onset- and midpoint-Tg at 301.1 and 306.7 °C and ρ = 5.62 g/cm3, in clear disagreement with TeO2 glass melted in alumina crucible for which we find Tg ≈ 380 °C and ρ = 4.86 g/cm3. This latter method, used frequently in the literature, was shown by Raman spectroscopy to introduce Al2O3 in the tellurite matrix which becomes cross-linked by Te-O-Al bridges, resulting in the increase of Tg and decrease of ρ. Raman spectroscopy showed also that doping TeO2 with ZnO or Al2O3 causes the progressive conversion of TeO4 trigonal bipyramids to TeO3 + 1 polyhedra with two terminal oxygens, and then to TeO3 trigonal pyramids with three terminal oxygens. This structural transformation is reflected in the composition dependence of the volume per mole TeO2 evaluated from density data. The ZnO-dependence of this parameter is described by two linear parts with an inflection point at x = 0.25, which indicates an increasing rate of forming terminal Te[sbnd]O bonds at higher ZnO contents. The Tg was found to increase with ZnO and Al2O3 contents and this was attributed to the glass-forming ability of both oxides, while density was found to decrease due mainly to replacement of the heavier TeO2 by the lighter ZnO and Al2O3. The results of this study are discussed with reference to previous works on TeO2 and zinc-tellurite glasses.
Τίτλος πηγής δημοσίευσης: Journal of Non-Crystalline Solids
Τόμος/Κεφάλαιο: 457
Σελίδες: 116-125
Θεματική Κατηγορία: [EL] Φυσική και θεωρητική χημεία[EN] Physical and theoretical chemistrysemantics logo
[EL] Φασματοσκοπία[EN] Spectroscopysemantics logo
Λέξεις-Κλειδιά: Alumino-tellurite glasses
Density
Glass structure
Glass transition temperature
Pure TeO2 glass
Raman spectroscopy
Zinc tellurite glasses
Αξιολόγηση από ομότιμους (peer reviewed): Ναι
Κάτοχος πνευματικών δικαιωμάτων: © 2016 Elsevier B.V.
Έχει σχέση με: Synthesis, structure and properties of pure TeO2 glass and tellurite glasses
Σημειώσεις: Εθνικό 'Ίδρυμα Ερευνών, EIE: 447963; General Secretariat for Research and Technology, GSRT
Financial support of this work by the General Secretariat for Research and Technology, Greece, through project POLYNANO?KRIPIS of TPCI/NHRF (??? 447963), is gratefully acknowledged..
Εμφανίζεται στις συλλογές:Ινστιτούτο Θεωρητικής και Φυσικής Χημείας (ΙΘΦΧ) - Επιστημονικό έργο

Αρχεία σε αυτό το τεκμήριο:
Το πλήρες κείμενο αυτού του τεκμηρίου δεν διατίθεται προς το παρόν από τον ΗΛΙΟ.