Τίτλος:	Phosphate structure and lithium environments in lithium phosphorus oxynitride amorphous thin films
Δημιουργός/Συγγραφέας:	Carrillo Solano M.A. Dussauze M. Vinatier P. Croguennec L. [EL] Καμίτσος, Ευστράτιος Ι.[EN] Kamitsos, Efstratios I. Hausbrand R. Jaegermann W.
Εκδότης:	Institute for Ionics
Ημερομηνία:	2016
Γλώσσα:	Αγγλικά
ISSN:	0947-7047
DOI:	10.1007/s11581-015-1573-1
Περίληψη:	Lithium ion-conducting glasses attract wide interest for electrochemical applications like efficient energy storage devices. This work presents a structural study on involved bonding units, based on X-ray photoelectron spectroscopy and infrared spectroscopy, of lithium phosphorus oxide and oxynitride amorphous thin films prepared by RF magnetron sputtering. A thorough consideration of the mid- and far-infrared spectral regions demonstrated structural changes at the phosphate units and the lithium ion environments triggered by nitrogen incorporation and post-deposition thermal treatment. It was found that films prepared by sputtering in pure nitrogen atmosphere have about 75 % of their nitrogen atoms in sites doubly coordinated with phosphorus (P–N=P), and the rest in triply coordinated sites. It was shown also that nitrogen incorporation favors the stability of lithium ions, while annealing enhances ionic conductivity of the oxynitride films.
Τίτλος πηγής δημοσίευσης:	Ionics
Τόμος/Κεφάλαιο:	22
Τεύχος:	4
Σελίδες:	471-481
Θεματική Κατηγορία:	[EL] Φυσική και θεωρητική χημεία[EN] Physical and theoretical chemistry [EL] Φασματοσκοπία[EN] Spectroscopy
Λέξεις-Κλειδιά:	Glasses IR spectroscopy LiPON Lithium phosphorus oxynitride Thin film
Αξιολόγηση από ομότιμους (peer reviewed):	Ναι
Κάτοχος πνευματικών δικαιωμάτων:	© 2015, Springer-Verlag Berlin Heidelberg.
Όροι και προϋποθέσεις δικαιωμάτων:	All Open Access, Green
Εμφανίζεται στις συλλογές:	Ινστιτούτο Θεωρητικής και Φυσικής Χημείας (ΙΘΦΧ) - Επιστημονικό έργο