Τίτλος:	Structural and luminescence behavior of Eu3+ ions in ZnO-B2O3-WO3 glasses
Δημιουργός/Συγγραφέας:	Milanova, M. Aleksandrov, L. Yordanova, A. Iordanova, R. Tagiara, N.S. Herrmann, A. Gao, G. Wondraczek, L. [EL] Καμίτσος, Ευστράτιος Ι.[EN] Kamitsos, Efstratios I.
Ημερομηνία:	2023
Γλώσσα:	Αγγλικά
ISSN:	00223093
DOI:	10.1016/j.jnoncrysol.2022.122006
Περίληψη:	Structure and luminescence properties of glasses with compositions 50ZnO:40B2O3:10WO3:xEu2O3, 0 ≤ x ≤ 10 mol% were studied using infrared, Raman and photoluminescence spectroscopic techniques. Physical properties like density, molar volume, oxygen molar volume and oxygen packing density of the glasses were also determined. The overall results obtained indicate the efficiency of the 50ZnO:40B2O3:10WO3 glass structure for the luminescence performance of doped Eu3+. The most intense luminescence peak observed at 612 nm and the high integrated emission intensity ratio (R) of the 5D0→7F2/5D0→7F1 transitions at 612 and 590 nm of 5.77 suggest that the glasses are potential materials for red emission. The results are compared to measurements of a glass without WO3 addition (50ZnO:50B2O3:5Eu2O3) and results from other publications of similar glasses.
Τίτλος πηγής δημοσίευσης:	Journal of Non-Crystalline Solids
Τόμος/Κεφάλαιο:	600
Θεματική Κατηγορία:	[EL] Φυσική και θεωρητική χημεία[EN] Physical and theoretical chemistry [EL] Φασματοσκοπία[EN] Spectroscopy
Λέξεις-Κλειδιά:	europium Raman glass structure melt quenching luminescence
EU Grant identifier:	КП-06-Н29/7 TwinTeam Д01-272/02.10.2020 г
Κάτοχος πνευματικών δικαιωμάτων:	© 2022 Elsevier B.V. All rights reserved.
Ηλεκτρονική διεύθυνση στον εκδότη (link):	https://doi.org/10.1016/j.jnoncrysol.2022.122006
Εμφανίζεται στις συλλογές:	Ινστιτούτο Θεωρητικής και Φυσικής Χημείας (ΙΘΦΧ) - Επιστημονικό έργο